Reduction and Reoxidation Processes of NiOYSZ Composite for Solid Oxide Fuel Cell Anodes

[+] Author and Article Information
Stefano Modena, Sergio Ceschini, Andrea Tomasi

ITC-Irst, Center for Scientific and Technological Research, v. Sommarive, 18 – 38050 Povo (TN), Italy

Dario Montinaro, Vincenzo M. Sglavo

Department of Materials Engineering and Industrial Technologies, University of Trento, v. Mesiano, 77 – 38050 Trento, Italy

J. Fuel Cell Sci. Technol 3(4), 487-491 (Mar 17, 2006) (5 pages) doi:10.1115/1.2349533 History: Received November 30, 2005; Revised March 17, 2006

Solid oxide fuel cells (SOFCs) are an emerging technology in hydrogen-based energy production, thanks to their high performance, high power density, high efficiency, and reduced emissions over conventional power generation technologies. For these reasons, a great attention has been addressed in these years to SOFCs materials and technologies. An important issue related to the utilization of SOFCs as power generators is the capability of SOFCs materials to resist to thermal cycles in different atmospheres. The present work proposes an experimental investigation on the reduction process of NiOYSZ anode into NiYSZ cermet, which is the best candidate for anode material in SOFCs, its reoxidation into NiOYSZ and the following rereduction into NiYSZ. Anodes with different NiOYSZ ratios were analyzed through different physical and chemical techniques, such as scanning electron microscopy (SEM) and porosity measurements. The reduction, reoxidation and rereduction behaviors were studied by thermogravimetric analysis (TGA) in a unique long experiment, at different temperatures in the range of 700–800°C. The kinetics of the processes was studied and thermodynamic parameters such as activation energy were also calculated and correlated to the compositions and microstructure of the materials. The study clears up the effect of anode composition and microstructure on the reduction, reoxidation, and rereduction processes.

Copyright © 2006 by American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.



Grahic Jump Location
Figure 1

SEM image of the typical microstructure after reduction of an anode supported SOFC

Grahic Jump Location
Figure 2

Normalized mass change versus time upon reduction for sample A (a) and sample B (b)

Grahic Jump Location
Figure 3

SEM images of the anode microstructure for sample A: (a) as prepared, (b) after reduction at 700°C; and (c) after reduction at 800°C

Grahic Jump Location
Figure 4

Normalized mass change versus logarithmic time upon oxidation for sample A (a) and sample B (b)

Grahic Jump Location
Figure 5

Normalized mass change versus time upon rereduction for sample A (a) and sample B (b)




Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In